Gegelung Keluli Tahan Karat 304 / 304L
| Spesifikasi | ASTM A240, ASME SA240 |
| Piawai | JIS, ASTM, AISI, GB, EN, DIN |
| Permukaan | 2B, BA, HL, No. 4, Cermin dll. |
| Selesai | Dingin, digulung panas |
| Ketebalan | 0.3mm – 100mm |
| Saiz | 1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm |
Spesifikasi Gred untuk Gelung Stainless Steel 304 / 304L
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | HADIAH | SELEPAS | EN |
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18‐09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18‐10 | X2CrNi18-9 / X2CrNi19-11 |
Sifat Kimia gegelung SS 304 / 304L
| Gred | C | Mn | Si | P | S | Cr | Mo | Ni | N |
| SS 304 | Maksimum 0.08 | 2 maks | Maksimum 0.75 | Maksimum 0.045 | Maksimum 0.030 | 18 - 20 | - | 8 - 11 | - |
| SS 304L | Maksimum 0.035 | 2 maks | 1.0 maks | Maksimum 0.045 | Maksimum 0.03 | 18 - 20 | - | 8 - 13 | - |
Sifat Mekanikal Gegelung SS 304 / 304L
| Gred / Temper | Tarik tegangan (min.) | Kekuatan Hasil 0.2% ksi (min.) | Pemanjangan -% dalam 50 mm (min.) | |
| Ketumpatan | Takat lebur | Kekuatan tegangan | Kekuatan Hasil (Offset 0.2%) | Pemanjangan |
| 8.0 g / cm3 | 1400 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |