Gegelung Keluli Tahan Karat 316 / 316L
| Spesifikasi | ASTM A240, ASME SA240 |
| Piawai | JIS, ASTM, AISI, GB, EN, DIN |
| Permukaan | 2B, BA, HL, No. 4, Cermin dll. |
| Selesai | Dingin, digulung panas |
| Ketebalan | 0.3mm – 100mm |
| Saiz | 1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm |
Spesifikasi Gred untuk Gegelung Keluli Tahan Karat 316 / 316L
| STANDARD | WERKSTOF No. | UNS | JIS | BS | HADIAH | SELEPAS | EN |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
Sifat Kimia gegelung SS 316 / 316L
| Gred | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 316 | Maksimum 0.08 | 2.0 maks | 1.0 maks | Maksimum 0.045 | Maksimum 0.030 | 16.00 - 18.00 | 2.00 - 3.00 | 11.00 - 14.00 | 67.845 min |
| SS 316L | Maksimum 0.035 | 2.0 maks | 1.0 maks | Maksimum 0.045 | Maksimum 0.030 | 16.00 - 18.00 | 2.00 - 3.00 | 10.00 - 14.00 | 68.89 min |
Sifat Mekanikal Gegelung SS 316 / 316L
| Ketumpatan | Takat lebur | Kekuatan tegangan | Kekuatan Hasil (Offset 0.2%) | Pemanjangan |
| 8.0 g / cm3 | 1400 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |
| 8.0 g / cm3 | 1399 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |