Gegelung Keluli Tahan Karat 420 / 420J1 / 420J2
| Spesifikasi | ASTM A240, ASME SA240 |
| Piawai | JIS, ASTM, AISI, GB, EN, DIN |
| Permukaan | 2B, BA, HL, No. 4, Cermin dll. |
| Selesai | Dingin, digulung panas |
| Ketebalan | 0.3mm ~ 200mm |
| Saiz | 0.3mm ~ 200mm |
| Panjang | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, dll |
| Lebar | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, dll |
Spesifikasi Gred untuk Gegelung Keluli Tahan Karat 420 / 420J1 / 420J2
| STANDARD | WERKSTOFF NR. | UNS | EN | BS | SELEPAS | SIS | JIS | AISI |
| SS 420 | 1.4021 | S42010 | X20Cr13 | 420S29 / 420S37 | - | 2303 | SUS420J1 | 420 |
| SS 420J1 | 1.4021 | S42010 | X20Cr13 | 420S29 | Z20C13 | 2303 | SUS420J1 | 420L |
| SS 420J2 | 1.4028 | S42000 | X20Cr13 | 420S37 | Z20C13 | 2304 | SUS420J2 | 420M |
Sifat Kimia gegelung SS 420 / 420J1 / 420J2
| Gred | C | Si | Mn | P | S | Cr |
| SS 420 | 0.16 - 0.25 | maksimum 1 | maksimum 1.5 | maksimum 0.04 | maksimum 0.015 | 12 - 14 |
Sifat Mekanikal Gegelung SS 420 / 420J1 / 420J2
| Rm - Kekuatan tegangan (MPa) (+ QT) | 650-950 |
| Rp0.2 0.2% kekuatan bukti (MPa) (+ QT) | 450-600 |
| KV - Tenaga impak (J) membujur., (+ QT) | + 20 ° 20-25 |
| A - Min. pemanjangan pada patah (%) (+ QT) | 10-12 |
| Kekerasan Vickers (HV): (+ A) | 190 - 240 |
| Kekerasan Vickers (HV): (+ QT) | 480 - 520 |
| Kekerasan Brinell (HB): (+ A)) | 230 |