Bar keluli tahan karat 17-4PH / SUS630
| MAKAN | ASTM | AISI | UNS | JIS | Yang lain |
| 1.4542 | |||||
| X5CrNiCuNb16-4 | Gred 630 | 630 | S17400 | SUS 630 | 17-4PH |
| AMS 5643 | |||||
| AMS 5622 | |||||
| Z6CNU17-04 | |||||
| 10705GU-GV |
Komposisi kimia ( %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Yang lain |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.07 | ≤ 1.00 | ≤ 1.00 | ≤ 0.040 | ≤ 0.030 | 15.0 ～ 17.0 | 3.00 ～ 5.00 | - | Cu 3.00 ～ 5.00 Nb + Ta 0.15 ～ 0.45 |
Sifat Mekanikal
| Keadaan rawatan haba | Tarik tegang Rm (MPa) | Hasil Rp0.2 (MPa) | Pemanjangan A (%) | Pengurangan silang bahagian mengenai patah tulang Z (%) | Kesannya AKV / AKU (J) | Brinell Kekerasan (HBW) |
|---|---|---|---|---|---|---|
| Disepuh | ≤ 1034 | ≤ 650 | 6.0 ～ 15.0 | 30.0 ～ 60.0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14.0 | ≥ 50.0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14.0 | ≥ 54.0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15.0 | ≥ 56.0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16.0 | ≥ 58.0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17.0 | ≥ 58.0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19.0 | ≥ 60.0 | ≥ 68 | ≤ 311 |
| H1150 + H1150 | ≥ 965 | ≥ 760 | ≥ 20.0 | ≥ 60.0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22.0 | ≥ 68.0 | ≥ 135 | ≤ 277 |
Bentuk dan Bentuk:
Palang bulat (Diameter): 5.5 mm hingga 700 mm
Batang dawai (Diameter): 0.10 ~ 16mm
Bar persegi / bar rata: 5mm hingga 550mm
Jalur keluli melalui penggulung sejuk: T0.1 - 3mm X W5 - 650mm XL (atau dalam bentuk gegelung)
Cincin palsu: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Plat berat / tengah melalui hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Potongan penempaan: batang aci dengan sayap / cakera / tiub / slug / donat / kiub / bentuk lain berdasarkan OEM.
Panjang: Panjang tetap atau panjang rawak atau berdasarkan keperluan khas pelanggan.